AbstractAbstractPellets pressed from WO3, Al, and fused Al2O3 powder mixes according to the stoichiometry 3Al + WO3 + xAl2O3 = (x + 1)Al2O3 + W (x = 0·1-0·5) were heated at 1473, 1623, and 1773 K for 3 h under coke granules. The composition and microstructure of samples were examined by X-ray diffraction analysis, scanning electron microscopy, and energy dispersive X-ray analysis. The products of the Al-WO3 reaction were found to consist of tungsten, corundum, and tungsten carbides. For x ≤ 0·3, temperature had little effect on the X-ray intensity ratios (IWC(101) + IW2C(101)) / IW(101) and IWC(101) / IW2C(101), whereas at x = 0·5 the influence of temperature was significant. Tungsten was converted to tungsten carbides in the samples heated at 1773 K. High temperature improved diffusion in the tungsten carbide layer and promoted the transformations from W to WC and from W2C to WC. Sintering of the corundum and tungsten resulted in cracks that provided rapid diffusion pathways for CO to penetrate and react with W.Keywords: ALUMINATUNGSTENCOMPOSITESYNTHESISMICROSTRUCTURE

Composition of Al₂O₃-W-WC composite prepared by WO₃-Al reaction under coke

ivySCI AI Smartly Parses PDF, Answers Researchers' Questions, and Helps You Understand Papers in Seconds

Journal Info

Composition of Al2O3-W-WC composite prepared by WO3-Al reaction under coke

ivySCI AI Smartly Parses PDF, Answers Researchers' Questions, and Helps You Understand Papers in Seconds

Journal Info

Composition of Al₂O₃-W-WC composite prepared by WO₃-Al reaction under coke